Japan JIS SFCM980R 鉻鉬鋼鍛鋼件 and Mechanical Properties, Chemical Element, Cross Reference.
Category | Grade | Standard | Region/Area | Standard Content |
---|---|---|---|---|
Metals | SFCM 980 R | JIS G3221 | Japan | 鉻鉬鋼鍛鋼件 |
Element | Min | Max | Similar |
---|---|---|---|
Si | 0.1500 | 0.3500 | - |
S | - | 0.0300 | - |
P | - | 0.0300 | - |
Mo | 0.1500 | 0.3000 | - |
Mn | 0.3000 | 0.8500 | - |
Cu | - | 0.3000 | - |
Cr | 0.9000 | 1.5000 | - |
C | - | 0.4800 | - |
Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV/Ku (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
---|---|---|---|---|---|---|
896 (≥) | 227 (≥) | 13 | 12 | 13 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 111 |
Temperature (°C) |
Modulus of elasticity (GPa) |
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and | Thermal conductivity (W/m·°C) |
Specific thermal capacity (J/kg·°C) |
Specific electrical resistivity (Ω mm²/m) |
Density (kg/dm³) |
Poisson’s coefficient, ν |
---|---|---|---|---|---|---|---|
31 | - | - | 0.42 | - | |||
996 | 191 | - | 14.3 | 243 | - | ||
362 | - | 22 | 12.2 | 433 | 141 |
Heat treated : 1548°C - 1659°C
Grade | Standard | Country | Application |
---|---|---|---|
ASTM 5140 | |||
AISI 201 | |||
AISI 202 | |||
1.2767 | |||
17-4PH | |||
AISI 1052 | |||
AISI 416Se | |||
AISI 1330 | |||
AISI 205 Stainless Steel | |||
AISI A10 | |||
AISI A2 | |||
AISI A3 | |||
AISI A4 | |||
1.0036 | |||
1.0037 | |||
SAE J403 | |||
UNS G10100 | |||
AMS 4924 | |||
ASTM A36 | |||
Electrode 100S-1 |
Our main peoducts of steel are many kinds of special steel, like tool steel, mould steel, alloy steel, alloy constructural steel, heat-resistant steel, high speed tool steel,spring steel and bearing steel , stainless steel and so on, which have formed 12 series and more than 350 varieties with n...
Rfq.: sales@longhaisteel.com