Ti 10-2-3 Ti Alloy
Our advantages
Ti 10-2-3 properties and heat treatment forged piece, Including Ti 10-2-3 application and specifications, We have all specifications,Including Ti 10-2-3 steel plate, Ti 10-2-3 sheet, Ti 10-2-3 square steel, Ti 10-2-3 flat bar,Ti 10-2-3 round bar,Ti 10-2-3 forgings, we can own production and sales.
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
forged/hot rolling/ extrusion of steel
We can produce the Ti 10-2-3 has the following specifications:
Round bar steel: 1mm to 3000mm
Square-shape steel: 1mm to 2000mm
Plate steel:0.1mm to 2500mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Chemical composition % of the ladle analysis of grade Ti 10-2-3 and Standards
Titanium Ti-10V-2Fe-3Al (Ti 10-2-3) Solution Treated 850°C (1560°F)
Categories: Metal; Nonferrous Metal; Titanium Alloy; Beta Titanium Alloy
Material Notes: 5 other heat treatments of this alloy are in MatWeb.
Key Words: KS 10-2-3; Ti 10-2-3; TIMETAL 10-2-3
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 4.65 g/cc | 0.168 lb/in³ | |
Mechanical Properties | Metric | English | Comments |
Tensile Strength, Ultimate | 1000 MPa | 145000 psi | |
Tensile Strength, Yield | 930 MPa | 135000 psi | |
Elongation at Break | 17.0 % | 17.0 % | |
Modulus of Elasticity | 110 GPa | 16000 ksi | unspecified heat treatment |
Poissons Ratio | 0.330 | 0.330 | Typical for beta titanium alloy. |
Fracture Toughness | 110 MPa-m½ | 100 ksi-in½ | K(IC) |
Shear Modulus | 41.0 GPa | 5950 ksi | |
Electrical Properties | Metric | English | Comments |
Electrical Resistivity | 0.000150 ohm-cm | 0.000150 ohm-cm | Estimated from similar high-V-stabilized beta titanium alloys. |
Thermal Properties | Metric | English | Comments |
CTE, linear |
9.70 µm/m-°C @Temperature 20.0 - 100 °C |
5.39 µin/in-°F @Temperature 68.0 - 212 °F |
|
9.70 µm/m-°C @Temperature 20.0 - 425 °C |
5.39 µin/in-°F @Temperature 68.0 - 797 °F |
average after ST 760ºC; Age 525ºC | |
Specific Heat Capacity | 0.525 J/g-°C | 0.125 BTU/lb-°F | Typical value for titanium alloys. |
Thermal Conductivity | 7.80 W/m-K | 54.1 BTU-in/hr-ft²-°F | Estimated from similar high-V-stabilized beta titanium alloys. |
Maximum Service Temperature, Air | 315 °C | 599 °F | |
Beta Transus | 760 °C | 1400 °F | |
Component Elements Properties | Metric | English | Comments |
Aluminum, Al | 2.60 - 3.40 % | 2.60 - 3.40 % | |
Carbon, C | <= 0.0500 % | <= 0.0500 % | |
Hydrogen, H | <= 0.0150 % | <= 0.0150 % | |
Iron, Fe | 1.60 - 2.20 % | 1.60 - 2.20 % | |
Nitrogen, N | <= 0.0500 % | <= 0.0500 % | |
Other, each | <= 0.100 % | <= 0.100 % | |
Other, total | <= 0.300 % | <= 0.300 % | |
Oxygen, O | <= 0.130 % | <= 0.130 % | |
Titanium, Ti | 82.855 - 86.8 % | 82.855 - 86.8 % | As Balance; Elemental Compostions per ASTM B265 |
Vanadium, V | 9.00 - 11.0 % | 9.00 - 11.0 % |
Users viewing this material also viewed the following:
Titanium Ti-10V-2Fe-3Al (Ti 10-2-3) ST 760°C, Aged 385°C
Titanium Ti-10V-2Fe-3Al (Ti 10-2-3) ST 760°C; Age 525°C (980°F)
Titanium Ti-10V-2Fe-3Al (Ti 10-2-3) ST 815°C, Anneal 620°C
Titanium Ti-10V-2Fe-3Al (Ti 10-2-3) ST 730°C; overage 580°C
Titanium Ti-10V-2Fe-3Al (Ti 10-2-3), Anneal 1 hr. 760°C
MTB020 / 14144
Machining performance
Download Ti 10-2-3 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.