Ti15Mo5Zr3Al Ti Alloy
Our advantages
Ti15Mo5Zr3Al properties and heat treatment forged piece, Including Ti15Mo5Zr3Al application and specifications, We have all specifications，Including Ti15Mo5Zr3Al steel plate, Ti15Mo5Zr3Al sheet, Ti15Mo5Zr3Al square steel, Ti15Mo5Zr3Al flat bar,Ti15Mo5Zr3Al round bar,Ti15Mo5Zr3Al forgings, we can own production and sales.
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
forged/hot rolling/ extrusion of steel
We can produce the Ti15Mo5Zr3Al has the following specifications:
Round bar steel: 1mm to 3000mm
Square-shape steel: 1mm to 2000mm
Plate steel:0.1mm to 2500mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Chemical composition % of the ladle analysis of grade Ti15Mo5Zr3Al and Standards
Ti15Mo5Zr3Al ß titanium alloy
Categories: Metal; Nonferrous Metal; Titanium Alloy; Beta Titanium Alloy
Key Words: medical, surgical
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 882 MPa | 128000 psi | solution heat treatment at 840°C |
| 882 - 1177 MPa | 128000 - 170700 psi | as forged and aged (600°C) | |
| 1099 MPa | 159400 psi | solution heat treatment at 740°C + aged at 600°C | |
| Tensile Strength, Yield | 870 MPa | 126000 psi | 0.2%, solution heat treatment at 840°C |
| 870 - 1173 MPa | 126000 - 170100 psi | as forged and aged (600°C) | |
| 1087 MPa | 157700 psi | 0.2%, solution heat treatment at 740°C + aged at 600°C | |
| Elongation at Break | 15.3 % | 15.3 % | solution heat treatment at 740°C + aged at 600°C |
| 15.0 - 20.0 % | 15.0 - 20.0 % | as forged and aged (600°C) | |
| 20.0 % | 20.0 % | solution heat treatment at 840°C | |
| Reduction of Area | 57.5 % | 57.5 % | solution heat treatment at 740°C + aged at 600°C |
| 43.0 - 80.0 % | 43.0 - 80.0 % | as forged and aged (600°C) | |
| 83.2 % | 83.2 % | solution heat treatment at 840°C | |
| Modulus of Elasticity | 75.0 GPa | 10900 ksi | Solution heat treated at 840°C |
| 88.0 GPa | 12800 ksi | Solution heat treated at 740°C | |
| 113 GPa | 16400 ksi | Solution heat treated at 740°C + aged at 600°C | |
| Component Elements Properties | Metric | English | Comments |
| Aluminum, Al | 3.80 % | 3.80 % | |
| Molybdenum, Mo | 15.0 % | 15.0 % | |
| Titanium, Ti | 76.2 % | 76.2 % | |
| Zirconium, Zr | 5.0 % | 5.0 % | |
Users viewing this material also viewed the following:
Titanium, Ti
Ti30Nb ß titanium alloy
Overview of materials for Beta Titanium Alloy
Ti6Al7Nb ASTM F1295
Ti30Ta ß titanium alloy
MMEDIC26 / 12402
Machining performance
Download Ti15Mo5Zr3Al the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.