Ti30Ta Ti Alloy
Our advantages
Ti30Ta properties and heat treatment forged piece, Including Ti30Ta application and specifications, We have all specifications,Including Ti30Ta steel plate, Ti30Ta sheet, Ti30Ta square steel, Ti30Ta flat bar,Ti30Ta round bar,Ti30Ta forgings, we can own production and sales.
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
forged/hot rolling/ extrusion of steel
We can produce the Ti30Ta has the following specifications:
Round bar steel: 1mm to 3000mm
Square-shape steel: 1mm to 2000mm
Plate steel:0.1mm to 2500mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Chemical composition % of the ladle analysis of grade Ti30Ta and Standards
Ti30Ta ß titanium alloy
Categories: Metal; Nonferrous Metal; Titanium Alloy; Beta Titanium Alloy
Key Words: medical, surgical
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 740 MPa | 107000 psi | as rolled |
800 MPa | 116000 psi | annealed at 1100°C | |
800 MPa | 116000 psi | annealed at 1400°C | |
Tensile Strength, Yield | 590 MPa | 85600 psi | as rolled |
650 MPa | 94300 psi | 0.2%, annealed at 1100°C | |
680 MPa | 98600 psi | 0.2%, annealed at 1400°C | |
Elongation at Break | 6.00 % | 6.00 % | annealed at 1400°C |
8.00 % | 8.00 % | annealed at 1100°C | |
28.0 % | 28.0 % | as rolled | |
Reduction of Area | 18.0 % | 18.0 % | annealed at 1400°C |
42.0 % | 42.0 % | annealed at 1100°C | |
58.0 % | 58.0 % | as rolled | |
Modulus of Elasticity | 63.0 GPa | 9140 ksi | 1h / 1000°C / water |
80.0 GPa | 11600 ksi | As rolled | |
Component Elements Properties | Metric | English | Comments |
Tantalum, Ta | 30.0 % | 30.0 % | |
Titanium, Ti | 70.0 % | 70.0 % |
Users viewing this material also viewed the following:
Ti30Nb ß titanium alloy
Ti15Mo5Zr3Al ß titanium alloy
Overview of materials for Beta Titanium Alloy
Titanium Alloys, General
Ti12Mo5Zr5Sn ß titanium alloy
MMEDIC29 / 12405
Machining performance
Download Ti30Ta the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.