Germany DIN X6Cr13 Stainless Steel and Mechanical Properties, Chemical Element, Cross Reference, Datasheet.
Category | Type | Steel Grade | Standard | Country | Application |
---|---|---|---|---|---|
Steel Grades | Stainless Steel | X6Cr13 | DIN | Germany | |
ASTM 5140 |
|||||
AISI 201 |
|||||
AISI 202 |
|||||
17-4PH |
|||||
AISI 416Se |
|||||
AISI 205 Stainless Steel |
|||||
00Cr18Ni5Mo3Si2 |
|||||
1Cr18Ni11SiA1Ti |
|||||
0Cr26Ni5Mo2 |
|||||
410CB |
C |
Si ≤ |
Mn ≤ |
P ≤ |
S ≤ |
Cr | Ni | Mo | Other |
---|---|---|---|---|---|---|---|---|
≤0.08 | 1.00 | 1.00 | 0.040 | 0.015 | 12.0-14.0 |
X6Cr13 ferritic stainless steel is contained in one of the lowest amount Cr.
It has good plastic, toughness and cold formability, and better than the other higher volume containing Cr ferritic stainless steel.
When X6Cr13 steel contains C quantity control very low, its plastic, especially the toughness, cold forming sex will also significantly enhanced.
X6Cr13 ferritic stainless steel is contained in one of the lowest amount Cr.
X6Cr13 steel is mainly used to produce resistance to steam, heat oil of sulfur corrosion components and/or equipment such as the lining.
Characteristics: used for high toughness and impact load parts.
USES: as turbine blade, structural frame, stainless equipment, lining, bolts, nuts, etc.
X6Cr13 chemical composition
Carbon C: more than 0.08
Si Si: more than 1.00
Manganese Mn: more than 1.00
Sulfur S: more than 0.030
Phosphorus P: more than 0.035
Chromium Cr: 11.50 ~ 13.50
Ni Ni: more than 0.60
X6Cr13 mechanical properties:
Tensile strength σ b (MPa) : quenching tempering, frequency 490
Conditions yield strength σ 0.2 (MPa) : quenching tempering, frequency 345
Elongation δ 5 (%) : quenching tempering, 24 frequency
Area reduction ψ (%) : quenching tempering, 60 frequency
Hardness: annealing, than 183 HB
X6Cr13 heat treatment standard and metallographic organization
Heat treatment specification: annealing, 800 ~ 900 ℃ slow cold or about 750 ℃ quick cold; 2) quenching (solid solution), 950 ~ 1000 ℃ cold oil; 3) the tempering, 700 ~ 750 ℃ soon cold.
Metallographic organization: organization feature for markov figure.
The surface: black, white and bright acid
Execution standard: GB, American standard ASTM, has obtained the IS09001 standard authentication.
Areas of application: stainless steel bars are widely used in stainless steel stamping, stainless steel tensile instruments, stainless steel decoration materials, electronic components, stamping, petroleum chemical packing, auto parts, fasteners, door top, bolt, hinge in shaft, cold-formed steel, rail slippery course, medical equipment, etc.
.
Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV/Ku (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
---|---|---|---|---|---|---|
362 (≥) | 647 (≥) | 41 | 21 | 31 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 224 |
Temperature (°C) |
Modulus of elasticity (GPa) |
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and | Thermal conductivity (W/m·°C) |
Specific thermal capacity (J/kg·°C) |
Specific electrical resistivity (Ω mm²/m) |
Density (kg/dm³) |
Poisson’s coefficient, ν |
---|---|---|---|---|---|---|---|
23 | - | - | 0.33 | - | |||
562 | 926 | - | 43.3 | 243 | - | ||
415 | - | 42 | 32.2 | 412 | 134 |
Heat treated : 1194°C - 1761°C
Grade | Standard | Country | Application |
---|---|---|---|
X6Cr13 | AFNOR | France | Ferritic |
ISO X6Cr13 | ISO standard thermal deformation of stainless steel | ||
EN X6Cr13 | EN | Euronorm Stainless Steel | |
EN X6Cr13 | EN | Euronorm Stainless Steel | |
EN X6Cr13 | EN | Euronorm Stainless Steel |
Our main peoducts of steel are many kinds of special steel, like tool steel, mould steel, alloy steel, alloy constructural steel, heat-resistant steel, high speed tool steel,spring steel and bearing steel , stainless steel and so on, which have formed 12 series and more than 350 varieties with n...
Rfq.: sales@longhaisteel.com