China GBT ZG08Cr19Ni11Mo3(ZG0Cr19Ni11Mo3) Heavy stainless steel castings and ZG08Cr19Ni11Mo3(ZG0Cr19Ni11Mo3) Mechanical Properties, Chemical Element, Cross Reference, Datasheet.
Category | Type | Steel Grade | Standard | Country | Application |
---|---|---|---|---|---|
Steel Grades | Special Alloy | ZG08Cr19Ni11Mo3(ZG0Cr19Ni11Mo3) | GBT | China | Heavy stainless steel castings |
ZG1Cr17Mn9Ni4Mo3Cu2N |
|||||
ZG1Cr18Mn13Mo3CuN |
|||||
ZG0Cr17Ni4CuNb |
|||||
ZG15Cr13(ZG1Cr13) |
|||||
ZG20Cr13(ZG2Cr13) |
|||||
ZG30Cr13(ZG3Cr13) |
|||||
ZG12Cr18Ni9Ti(ZG12Cr18Ni9Ti) |
|||||
ZG06Cr13Ni4Mo(ZG0Cr13Ni4Mo) |
|||||
ZG06Cr13Ni6Mo(ZG0Cr13Ni6Mo) |
|||||
ZG08Cr19Ni9(ZG0Cr19Ni9) |
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Ni(%) | Mo(%) |
---|---|---|---|---|---|---|---|
≤0.08 | ≤1.50 | ≤1.50 | 0.04 | 0.04 | 18.0-21.0 | 9.00-13.00 | 3.00-4.00 |
Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV/Ku (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
---|---|---|---|---|---|---|
832 (≥) | 814 (≥) | 34 | 43 | 44 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 311 |
Temperature (°C) |
Modulus of elasticity (GPa) |
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and | Thermal conductivity (W/m·°C) |
Specific thermal capacity (J/kg·°C) |
Specific electrical resistivity (Ω mm²/m) |
Density (kg/dm³) |
Poisson’s coefficient, ν |
---|---|---|---|---|---|---|---|
13 | - | - | 0.31 | - | |||
495 | 247 | - | 24.3 | 424 | - | ||
571 | - | 44 | 14.2 | 312 | 312 |
Heat treated : 1545°C - 1119°C
Grade | Standard | Country | Application |
---|---|---|---|
ZG08Cr19Ni11Mo3(ZG0Cr19Ni11Mo3) | GBT | China | Heavy stainless steel castings |