USA SAE A 814/A 814M (2008) , A 814 S30409 Specialsteel Cold-Worked Welded Austenitic Stainless Steel Pipe and Mechanical Properties, Chemical Element, Cross Reference, Datasheet.
Category | Class | Grade | Type | Standard | Country | Application |
---|---|---|---|---|---|---|
Steel Grades | Specialsteel | A 814 S30409 | Austenite | SAE | USA | Cold-Worked Welded Austenitic Stainless Steel Pipe |
C | Si | Mn | P | S | Cr | Ni |
---|---|---|---|---|---|---|
0.04 -0.10 | ≤1.00 | ≤2.00 | ≤0.04 | ≤0.03 | 18.0 -20.0 | 8.00 -11.0 |
Yield Rp0.2 (MPa) |
Tensile Rm (MPa) |
Impact KV/Ku (J) |
Elongation A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
---|---|---|---|---|---|---|
322 (≥) | 199 (≥) | 44 | 41 | 33 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 114 |
Temperature (°C) |
Modulus of elasticity (GPa) |
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and | Thermal conductivity (W/m·°C) |
Specific thermal capacity (J/kg·°C) |
Specific electrical resistivity (Ω mm²/m) |
Density (kg/dm³) |
Poisson’s coefficient, ν |
---|---|---|---|---|---|---|---|
11 | - | - | 0.22 | - | |||
549 | 327 | - | 24.3 | 111 | - | ||
185 | - | 13 | 32.2 | 143 | 422 |
Heat treated : 1831°C - 1877°C
Grade | Standard | Country | Application |
---|---|---|---|
304H | |||
304HN | |||
304HN | |||
304H | |||
TP304H | |||
TP304H | |||
TP304H | |||
SUS304HFB | |||
SUS304HTP | |||
SUS304HTB | |||
SUS304HTB | |||
SUS304HTP | |||
SUS304HFB | |||
304HN(S30452) | |||
SUS304HFB | |||
SUS304HFB | |||
SUS304HTP | |||
SUS304HTP | |||
S30409 | |||
S30409 |
A 814/A 814M (2008) | Cold-Worked Welded Austenitic Stainless Steel Pipe | A-814-A-814M--(2008)-.pdf |
Our main peoducts of steel are many kinds of special steel, like tool steel, mould steel, alloy steel, alloy constructural steel, heat-resistant steel, high speed tool steel,spring steel and bearing steel , stainless steel and so on, which have formed 12 series and more than 350 varieties with n...
Rfq.: sales@longhaisteel.com