3.7035 Ti Alloy

This page provides 3.7035 Ti Alloy datasheet, 3.7035 Ti Alloy mechanical properties, chemical element 3.7035 Ti Alloy, technical specifications of 3.7035 Ti Alloy steel material properties. 3.7035 Ti Alloy performance specifications.

Category Class Grade Standard Country Application
Steel GradesTi Alloy 3.7035 Ti Alloy
Datasheet for:Steel Grades:Ti Alloy:3.7035 Ti Alloy

Chemical composition(mass fraction)(wt.%) of the 3.7035 Ti Alloy

Our to produce better steel-based products are the main used in industrial manufacturing various types Ti Alloy3.7035 plate,3.7035 Round Bar,3.7035 forgings,3.7035 suppliers, 3.7035 Stock,3.7035 sheet, 3.7035 flat bar, 3.7035 pipe,3.7035 tube,3.7035 mould,3.7035 round ingot,3.7035 cold-rolled steel,3.7035 coil,3.7035 strap steel,3.7035 hot-rolled steel,3.7035 medium plate, 3.7035 heavy plate,3.7035 shapped bar,3.7035 hexahedral bar,3.7035,3.7035 slab ingot,3.7035 slab,3.7035 price,3.7035 square bar,3.7035 square steel,3.7035 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 3.7035.

Our advantages

3.7035 properties and heat treatment forged piece, Including 3.7035 application and specifications, We have all specifications,Including 3.7035 steel plate, 3.7035 sheet, 3.7035 square steel, 3.7035 flat bar,3.7035 round bar,3.7035 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 3.7035 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 3.7035 and Standards

3.7035

 

Material No. 3.7035
EN symbol (short) Ti-II
AISI/SAE
UNS R 50400
AFNOR
B.S.
Alloy
Registered work's label Ti 994-Ti-grade2
Standards DIN 17850

 

Description

Our product range in 3.7025 are tubes and pipes, fittings and flanges, accessories

 

Chemical composition

C
≤%
N
≤%
H
≤%
Fe
≤%
O
≤%
Pa
%
Others
%
Ti
 
0,08 0,06 0,013 0,25 0,20   0,4 rest

 

Special characteristics

Temperature range Density kg/dm³ Hardness HB
  approx. 4,5  
particularly good stability against corrosion, low specific weight, little cold-straining

 

Welding filler

Welding rod and wire electrode SG-Ti2

 

Main fields of application (depending on the specific conditions of use)

chemical industry, offshore platforms, aviation, space travel, highly stressed weight-saving components, condensers, sea water desalination plants, power stations



Machining performance

Download 3.7035 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:3.7035 steel plate, 3.7035 sheet, 3.7035 square steel, 3.7035 flat bar,3.7035 round bar,3.7035 forgings

Mechanical properties / Mechanische Eigenschaften / Caracteristiques mecaniques of grade 3.7035 Ti Alloy

Yield
Rp0.2 (MPa)
Tensile
Rm (MPa)
Impact
KV/Ku (J)
Elongation
A (%)
Reduction in cross section on fracture
Z (%)
As-Heat-Treated Condition Brinell hardness (HBW)
951 (≥) 827 (≥) 34 24 43 Solution and Aging, Annealing, Ausaging, Q+T,etc 414
Temperature
(°C)
Modulus of elasticity
(GPa)
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and Thermal conductivity
(W/m·°C)
Specific thermal capacity
(J/kg·°C)
Specific electrical resistivity
(Ω mm²/m)
Density
(kg/dm³)
Poisson’s coefficient, ν
21 - -     0.31 -  
241 692 - 43.3 432   -  
328 - 34 33.2   211 444
Heat treated : 1766°C - 1527°C
Directory is being updated.
The material does not have direct Metallography properties.
Directory is being updated.
The material does not have direct Metallography properties.
Directory is being updated.
Cross Reference Table(Equivalent Grade)
Grade Standard Country Application
Y1Cr18Ni9 GB China
Improve the machinability, ablation resistance. Suitable for automatic lathe production of bolt and nut
1Cr18Ni9 GB China
High strength after cold forming, but elongation than 1 cr17ni7 slightly worse. Used in architectural decoration parts
1Cr18Mn10Ni5Mo3N GB China
Of urea with good corrosion resistance, can produce urea corrosion of the equipment.
1Cr17Ni7 GB China
High strength after cold forming. Used in railway vehicle, conveyor belt, bolt and nut, etc
Y1Cr18Ni9Se GB China
Improve the machinability, ablation resistance. Suitable for automatic lathe production of rivets, screws
0Cr18Ni9 GB China
Seamless stainless steel tubes for boiler and heat exchanger
00Cr19Ni10 GB China
Carbon content lower than 0Cr19ni9 steel, excellent intergranular corrosion resistance, is used for welding after the class is not processed parts
1Cr17Mn6Ni5N GB China
Nickel steel grade, instead of number 1 cr17ni7 and magnetism after cold working, used in railway vehicle, etc
1Cr18Mn8Ni5N GB China
Nickel steel, instead of 1cr18ni9
0Cr19Ni9N GB China
Based on 0cr19ni9 plus N, strength increase and the plastic is not down. Reduce the thickness of the material. As a structure with strength components
0Cr19Ni10NbN GB China
Based on zero cr19ni9 plus N and Nb, with better than 0 cr19ni9 properties and USES
00Cr18Ni10N GB China
In 00cr19ni10 adding N, on the basis of the above grades also features, use the same as the 0 cr19ni9n, but better intergranular corrosion resistance
1Cr18Ni12 GB China
Compared with 0 cr19ni9, processing low hardenability. Used for spinning processing, special drawing, cold heading
0Cr23Ni13 GB China
Corrosion resistance and heat resistance are better than 0cr19ni9
0Cr25Ni20 GB China
Oxidation resistance is better than 0cr23ni13. Mostly used as heat resistant steel
0Cr17Ni12Mo2 GB China
Seamless stainless steel tubes for boiler and heat exchanger
1Cr18Ni12Mo2Ti GB China
Seamless stainless steel tubes for boiler and heat exchanger
0Cr18Ni12Mo2Ti GB China
Seamless stainless steel tubes for boiler and heat exchanger
A-29 1025 SAE USA
General use carbon steel rod
1025 SAE USA
These products have been used typically for use in fabrication of fittings, but usage is not limited to such applications. These products are not typically used for deep forming or cupping operations.
3.7035 Ti Alloy Suppliers

Haihong International Trade (HK) CO., Limited

Stainless Steel, Special Steel, Compressor Blading, Turbine Blading, Superalloy Supplier.
3.7035 Ti Alloy can be supplied as steel plate/ sheet, round steel bar, steel tube/pipe, steel stripe, steel billet, steel ingot, steel wire rods. electroslag, forged ring/ block,etc.
TEL:+86-816-3646575 FAX: +86-816-3639422
M/B:+86-15386639257
E-mail: sales@tool-die-steels.com
Website: http://www.tool-die-steels.com/
Join Supplier: sales@steel-grades.com