99.2 Ti Ti Alloy

This page provides 99.2 Ti Ti Alloy datasheet, 99.2 Ti Ti Alloy mechanical properties, chemical element 99.2 Ti Ti Alloy, technical specifications of 99.2 Ti Ti Alloy steel material properties. 99.2 Ti Ti Alloy performance specifications.

AISI 99.2 Ti Ti Alloy AISI 99.2 Ti Ti Alloy Datasheet
Category Class Grade Standard Country Application
Steel GradesTi Alloy 99.2 Ti Ti Alloy AISI
Datasheet for:Steel Grades:Ti Alloy:99.2 Ti Ti Alloy

Chemical composition(mass fraction)(wt.%) of the 99.2 Ti Ti Alloy

 

Category Titanium Alloy
Class Wrought
Type Commercially Pure
Designations United States: ASTM B265 Grade2, ASTM B348 Grade2, ASTM B381 Grade2, MIL-T-9046, AMS 4942, AMS 4902, AMS 4941, AMS 4951
Composition
Element Weight %
Ti  99.2 

 

Mechanical Properties
Properties  Conditions
T (°C) Treatment
Density (×1000 kg/m3) 4.51 25  
Poisson's Ratio 0.34 25  
Elastic Modulus (GPa) 102.7 25  
Tensile Strength (Mpa) 193 315 more annealed  
Yield Strength (Mpa) 117
Elongation (%) 35 
Reduction in Area (%) 75 
Hardness (HB) 200  25 annealed 
Impact Strength (J)
(Charpy)
43 25 annealed  

 

Thermal Properties
Properties  Conditions
T (°C) Treatment
Thermal Expansion (10-6/ºC) 8.6 20-100 more  

<script type=text/javascript> </script><script src="http://pagead2.googlesyndication.com/pagead/show_ads.js" type=text/javascript> </script><script src="http://pagead2.googlesyndication.com/pagead/js/r20120130/r20110914/show_ads_impl.js"></script><script src="http://pagead2.googlesyndication.com/pagead/render_ads.js"></script><script>google_protectAndRun("render_ads.js::google_render_ad", google_handleError, google_render_ad);</script>
 

Mechanical properties / Mechanische Eigenschaften / Caracteristiques mecaniques of grade 99.2 Ti Ti Alloy

Yield
Rp0.2 (MPa)
Tensile
Rm (MPa)
Impact
KV/Ku (J)
Elongation
A (%)
Reduction in cross section on fracture
Z (%)
As-Heat-Treated Condition Brinell hardness (HBW)
225 (≥) 357 (≥) 11 41 44 Solution and Aging, Annealing, Ausaging, Q+T,etc 432
Temperature
(°C)
Modulus of elasticity
(GPa)
Mean coefficient of thermal expansion 10-6/(°C) between 20(°C) and Thermal conductivity
(W/m·°C)
Specific thermal capacity
(J/kg·°C)
Specific electrical resistivity
(Ω mm²/m)
Density
(kg/dm³)
Poisson’s coefficient, ν
22 - -     0.23 -  
247 525 - 33.3 334   -  
256 - 22 31.2   212 343
Heat treated : 1979°C - 1893°C
Directory is being updated.
The material does not have direct Metallography properties.
Directory is being updated.
The material does not have direct Metallography properties.
Directory is being updated.
Cross Reference Table(Equivalent Grade)
Grade Standard Country Application
Y1Cr18Ni9 GB China
Improve the machinability, ablation resistance. Suitable for automatic lathe production of bolt and nut
1Cr18Ni9 GB China
High strength after cold forming, but elongation than 1 cr17ni7 slightly worse. Used in architectural decoration parts
1Cr18Mn10Ni5Mo3N GB China
Of urea with good corrosion resistance, can produce urea corrosion of the equipment.
1Cr17Ni7 GB China
High strength after cold forming. Used in railway vehicle, conveyor belt, bolt and nut, etc
Y1Cr18Ni9Se GB China
Improve the machinability, ablation resistance. Suitable for automatic lathe production of rivets, screws
0Cr18Ni9 GB China
Seamless stainless steel tubes for boiler and heat exchanger
00Cr19Ni10 GB China
Carbon content lower than 0Cr19ni9 steel, excellent intergranular corrosion resistance, is used for welding after the class is not processed parts
1Cr17Mn6Ni5N GB China
Nickel steel grade, instead of number 1 cr17ni7 and magnetism after cold working, used in railway vehicle, etc
1Cr18Mn8Ni5N GB China
Nickel steel, instead of 1cr18ni9
0Cr19Ni9N GB China
Based on 0cr19ni9 plus N, strength increase and the plastic is not down. Reduce the thickness of the material. As a structure with strength components
0Cr19Ni10NbN GB China
Based on zero cr19ni9 plus N and Nb, with better than 0 cr19ni9 properties and USES
00Cr18Ni10N GB China
In 00cr19ni10 adding N, on the basis of the above grades also features, use the same as the 0 cr19ni9n, but better intergranular corrosion resistance
1Cr18Ni12 GB China
Compared with 0 cr19ni9, processing low hardenability. Used for spinning processing, special drawing, cold heading
0Cr23Ni13 GB China
Corrosion resistance and heat resistance are better than 0cr19ni9
0Cr25Ni20 GB China
Oxidation resistance is better than 0cr23ni13. Mostly used as heat resistant steel
0Cr17Ni12Mo2 GB China
Seamless stainless steel tubes for boiler and heat exchanger
1Cr18Ni12Mo2Ti GB China
Seamless stainless steel tubes for boiler and heat exchanger
0Cr18Ni12Mo2Ti GB China
Seamless stainless steel tubes for boiler and heat exchanger
A-29 1025 SAE USA
General use carbon steel rod
1025 SAE USA
These products have been used typically for use in fabrication of fittings, but usage is not limited to such applications. These products are not typically used for deep forming or cupping operations.
99.2 Ti Ti Alloy Suppliers

Haihong International Trade (HK) CO., Limited

Stainless Steel, Special Steel, Compressor Blading, Turbine Blading, Superalloy Supplier.
99.2 Ti Ti Alloy can be supplied as steel plate/ sheet, round steel bar, steel tube/pipe, steel stripe, steel billet, steel ingot, steel wire rods. electroslag, forged ring/ block,etc.
TEL:+86-816-3646575 FAX: +86-816-3639422
M/B:+86-15386639257
E-mail: sales@tool-die-steels.com
Website: http://www.tool-die-steels.com/
Join Supplier: sales@steel-grades.com